Sabra Metals, based in Amman, Jordan, has built a solid reputation as a reliable manufacturer and supplier of top-notch metal products. They specialize in dependable carbon-steel solutions, including the 1008 Round Bar. With a strong focus on precision engineering and consistent performance, Sabra Metals caters to a diverse range of industries throughout the region, from construction and fabrication to automotive applications. The company prides itself on sourcing high-quality materials, maintaining strict quality control, and providing customer-centric service, ensuring that every product meets international standards. Through ongoing innovation and a commitment to excellence, Sabra Metals has established itself as a trusted partner for all industrial metal needs.
The 1008 Round Bar is a low-carbon steel product that contains about 0.08% carbon, along with trace amounts of manganese, phosphorus, and sulfur. Its low carbon content gives it excellent ductility, formability, and weldability. In terms of mechanical properties, 1008 steel offers moderate tensile strength, good elongation, and notable softness, making it ideal for cold-working processes. Its relatively low yield strength allows for easy shaping without sacrificing structural integrity. These well-balanced characteristics make the 1008 Round Bar perfect for a wide range of manufacturing and forming applications.
|
Steel Grade |
C |
Mn |
Si |
P |
S |
Cr |
Ni |
B |
Cu |
Mo |
V |
|---|---|---|---|---|---|---|---|---|---|---|---|
|
55 |
0.52-0.60 |
0.50-0.80 |
0.17-0.37 |
0.035 max |
0.035 max |
0.25 max |
0.30 max |
/ |
0.25 max |
/ |
/ |
|
65 |
0.62-0.70 |
0.50-0.80 |
0.17-0.37 |
0.035 max |
0.035 max |
0.25 max |
0.25 max |
/ |
0.25 max |
/ |
/ |
|
70 |
0.62-0.75 |
0.50-0.80 |
0.17-0.37 |
0.035 max |
0.035 max |
0.25 max |
0.25 max |
/ |
0.25 max |
/ |
/ |
|
75 |
0.72-0.80 |
0.50-0.80 |
0.17-0.37 |
0.035 max |
0.035 max |
0.25 max |
0.30 max |
/ |
0.25 max |
/ |
/ |
|
85 |
0.95-1.04 |
0.40 max |
0.35 max |
0.025 max |
0.025 max |
/ |
/ |
/ |
/ |
/ |
/ |
|
65Mn |
0.62-0.70 |
0.90-1.20 |
0.17-0.37 |
0.035 max |
0.035 max |
0.25 max |
0.25 max |
/ |
0.25 max |
/ |
/ |
|
60Si2Mn |
0.56-0.64 |
0.70-1.00 |
1.50-2.00 |
0.035 max |
0.035 max |
0.35 max |
0.25 max |
/ |
0.25 max |
/ |
/ |
|
50CrVA |
0.46-0.54 |
0.50-0.80 |
0.17-0.37 |
0.025 max |
0.025 max |
0.80-1.10 |
0.35 max |
/ |
0.25 max |
/ |
0.10-0.20 |
|
55SiCrA |
0.51-0.59 |
0.50-0.80 |
1.20-1.60 |
0.025 max |
0.025 max |
0.50-0.80 |
0.35 max |
/ |
0.25 max |
/ |
/ |
|
60Si2CrA |
0.56-0.64 |
0.40-0.70 |
1.40-1.80 |
0.025 max |
0.025 max |
0.70-1.00 |
0.35 max |
/ |
0.25 max |
/ |
/ |
|
Steel Grade |
Tensile Strength Rm (Mpa) |
Yield Strength Rp0.2 (Mpa) |
Elongation A5 (%) |
Area Reduction Ratio C (%) |
|---|---|---|---|---|
|
65 |
980 min |
785 min |
9 min |
35 min |
|
70 |
1030 min |
835 min |
8 min |
30 min |
|
85 |
1130 min |
980 min |
6 min |
30 min |
|
65Mn |
980 min |
785 min |
8 min |
30 min |
|
60Si2Mn |
1275 min |
1180 min |
5 min |
25 min |
|
50CrVA |
1275 min |
1130 min |
10 min |
40 min |
|
55SiCrA |
1450-1750 |
1300 min |
6 min |
25 min |
|
60Si2CrA |
1765 min |
1570 min |
6 min |
20 min |
When selecting carbon steel spring bars, consider factors like the required strength, durability, and fatigue resistance for the specific application. Also, evaluate the environment's corrosion potential and the bar's ability to retain spring properties over time.
Carbon steel spring bars are generally not suitable for cryogenic applications due to their reduced toughness and brittleness at extremely low temperatures. Materials like stainless steel or special alloys are preferred for such conditions.
Carbon steel spring rods are available in various sizes, typically ranging from 1/4 inch to several inches in diameter, with lengths varying based on application requirements. Custom sizes can be manufactured to meet specific load, stress, or design needs.
Industries that require exceptional formability and reliable performance in low-stress conditions frequently use the 1008 Round Bar. It’s commonly found in the production of fasteners, wire products, small machine components, and cold-headed parts. In the automotive sector, it’s utilized for brackets, clamps, and lightweight structural elements. Thanks to its excellent weldability, it also plays a key role in fabrication projects, furniture manufacturing, and general engineering tasks. Additionally, the 1008 Round Bar is often chosen for drawing, bending, and stamping processes, consistently delivering reliable results across various industrial and commercial production environments.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.